Journal Name:
MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS
Volume:
178
Issue:
12
Pages From:
851
To:
856
Date:
الاثنين, يوليو 1, 2013
Keywords:
Metals and alloys; Vapor deposition; Thin films; Tunneling diodes
Abstract:
In this work, the design and characterization of magnesium oxide based tunneling diodes which are produced on Al and InSe films as rectifying substrates are investigated. It was found that when Al thin films are used, the device exhibit tunneling diode behavior of sharp valley at 0.15 V and peak to valley current ratio (PVCR) of 11.4. In addition, the capacitance spectra of the Al/MgO/C device show a resonance peak of negative capacitance (NC) values at 44.7 MHz. The capacitance and resistance-voltage characteristics handled at an ac signal frequency of 100 MHz reflected a build in voltage (V-bi) of 1.29 V and a negative resistance (NR) effect above 2.05 V. This device quality factor (Q)-voltage response is similar to 10(4). When the Al substrate is replaced by InSe thin film, the tunneling diode valley appeared at 1.1 V. In addition, the PVCR, NR range, NC resonance peak, Q and lib; are found to be 135, 0.94-2.24 and 39.0 MHz, similar to 10(5) and 1.34 V, respectively. Due to the wide differential negative resistance and capacitance voltage ranges and due to the response of the C/MgO/InSe/C device at 1.0 GHz, these devices appear to be suitable for applications as frequency mixers, amplifiers, and monostable-bistable circuit elements (MOBILE). (c) 2013 Elsevier B.V. All rights reserved.